Folacoat Extreme is the logical advanced development of the globally accepted Folacoat Plus.
Our Folacoat Extreme is particularly capable of meeting today's higher demands on print run stability when using UV coatings.
In addition, it is the perfect transfer medium for H-UV or LED-UV applications.
The two-layer polyester carrier permits very long runs and reduces the risk of rupturing of the carrier, particularly in the event of manual cutting. The slipping film additionally applied enables coating plates to be produced on a cutting plotter without difficulty, providing cut visualisation at the same time. As a result, all zones to be stripped are easily identifiable.
The Folacoat Extreme is now also available in roll-length 30m and 40m.
Please click here to find useful handling recommendation and interesting product introduction by video.
|Art. Number||Nominal thickness (inch)||Nominal thickness (mm)|
|Art. Number||Width (mm)||Length (m)||Nominal thickness (inch)||Nominal thickness (mm)|
- Best solution in H-UV application
- Recommended for direct coating
- Suitable for aqueous coating
- Suitable for UV coating
- Slipping film / protection film
- Ideal for CAD cutting systems
- Polyester-basis/ -carrier
- Cutting protection (double layer)
- Cut visualization
|Thickness of polymer layer||0.75 mm (.0295'')|
|Thickness of carrier material||0.39 mm (.0154'')|
|Tolerance of thickness||± 0.05 mm (.002'')|
|Type of coating transfer||direct coating|
|Plate hardness||88 Shore A|
|Nominal thickness (inch)||.045|
|Nominal thickness (mm)||1.15|
|Surface treatment||Slipping film/Protection film|
|Hardness of polymer (DIN 53505)||83 Shore A|
|Base Material||Polyester / Polyester|
- Best solution in H-UV and LED-UV applications.
- Suitable for aqueous and UV coatings. Increased resistance against UV coatings and cleaning agents
NOMINAL THICKNESS 1.35 mm: Recommended cutting depth about 0.85 mm (.0335”). If you like to remove the slipping film before cutting, reduce depth by 0.05 mm (.002”). The polyester film in the middle helps to avoid deformations of the carrier-film below. A thin white line on the reverse side of the plate indicates that the cut went through the entire polymer and scored slightly into the polyester ensuring the correct cutting depth has been reached. This now means the correct stripping performance will be obtained without the partial lifting of the remaining polymer areas.