Semi matt polyester film with anti reflective coating on the front side suitable for window printing with UV and 2 component lacquers. High UV and outdoor stability. The reverse side has an ink receptive coating for screen printing inks.

Material is available with a thickness of 0.13 mm, 0.18 mm and 0.25 mm. Available in sheets and rolls. Sheets available in standard packing unit or on demand. All sheets are equipped with interleaving paper as standard.

Cut sheets

Art. NumberNominal thickness (mm)Packing quantity
48064.130.xxxxx0.13100PDF
48064.180.xxxxx0.18100PDF
48064.250.xxxxx0.25100PDF

Rolls

Art. NumberLength (m)Nominal thickness (mm)
48064.130.xxxxx1000.13PDF
48064.180.xxxxx1000.18PDF
48064.250.xxxxx1000.25PDF

Technical data

Characteristic

  • Ink receptive coating
  • Suitable for window printing
  • Suitable for textured laquers
  • With UV protection

Excellent chemical resistance to common industrial solvents and household chemicals - please refer to Folex "Chemical Resistance Datasheet".


Folex products can be printed digital and screen in many cases with excellent results. We offer improved versions dedicated for digital printing.

Properties

PropertyTest MethodValue
ThicknessFolex test method0,13 - 0,14mm (0,13mm), 0,18-0,195mm (0,18mm), 0,255-0,27mm (0,25mm)
Optical
HazeASTM D1003-7735 - 45%
TransmissionASTM D1003-7789 - 91%
Gloss level (60°)ASTM D2457-70, ASTM D52323 - 29 GU
Yellowness IndexDIN 61671,22 (0,13mm), 1,19 (0,18mm), 1,83 (0,25mm)
Mechanical
EmbossingFolex methodpossible
Tensile strength at breakASTM D 882170 N/mm2
Switch lifeFolex method according to DIN 42115 > 5 Mio. flexes
Adhesion of coatingFolex methodpassed
Electrical
Breakdown Voltage1ASTM D 14916,5 kV (0,13mm)/ 19,0 kV (0,18mm)
Chemical
Chemical stabilityFolex methodgood
Electrical
Thermal
Shrinkage TD130°C 30 min Folex method< 0,7%
Shrinkage MD130°C 30 min Folex method< 0,7%
Maximum processing temperature120°C
Maximum use temp45°C/ 80°C (with embossing/ without embossing at 50%RH without condensation)
Minimum use temp0°C/ -20°C (with embossing/ without embossing at 50%RH without condensation)
Melting temperature1ASTM E794-85255°C
Relative thermal index-mechanical1ANSI/UL 746BRTI 105°C
Surface
Roughness RaEN ISO 4287, ASME B46.10,9 - 1,3 µm
Scratch resistanceFolex methodgood
Surface tension front side DIN 53364, ASTM D257835 ± 2 mN/m
Surface tension reverse sideDIN 53364, ASTM D257838 - 41 mN/m

1 Data derived from base film Polyester manufacturer's literature

Specifications

Nominal thickness (mil)5.2
Nominal thickness (mm)0.13
Base MaterialPolyester
Packing quantity 100

Product Applications

  • Suitable for Membrane Switches, sign production as well as for production of labels

Handling

  • Preliminary testing necessary by customer

Storage

  • Once packaging is opened, store at a room temperature of 15 - 25°C and at a humidity of 30 - 60 %